You are starting out wrestling the 800 lb gorilla . 6061 is not considered very workable . Most 6061 I see is T6 and would need annealing to be workable .
6061 typically will crack if bent 90 degrees very tightly .
Even if annealed, it is not very workable , it would be worth the investment to find 3003 .
|