Ken, I'm no expert on flow forming, but your material seems both pretty thick and pretty hard. Maybe try a little 3003 0.050 and anneal it first. Not sure what you are making, so this may not be strong enough, but at least you'll know if your problem is the tools or the material.
__________________
Steve Greenway
|